fabricated via high velocity air-fuel(HVAF) spraying technique. The microstructures of these coatings were characterized by means of metallographic microscopy, scanning electron microscopy, transmission... nanostructured NiCrC coating has a homogeneous nanocrystalline microstructure with an average grain size of 40 nm. Key words: HVAF spraying; nanostructure; coating; NiCrC; properties  ......
Thermal stability of nanostructured NiCrC coating prepared by HVAF spraying of cryomilled powdersCUI Hua a, TAO Kai b, ZHOU Xianglin b, and ZHANG Jishan b a School of Materials Science...:Thermal stability of nanostructured NiCrC coating prepared by high velocity air-fuel (HVAF) spraying of cryomilled feedstock powders was investigated......
HVAF喷涂WC-10Co4Cr涂层及其性能伏利1,2,3,周夏凉1,2,3,陈小明1,2,3,吴燕明1,2,王莉容3,4,赵坚3,4,刘伟1,21. 水利部产品质量标准研究所2. 浙江省水利水电装备表面工程技术研究重点实验室3. 水利机械及其再制造技术浙江省工程实验室4. 水利部杭州机械设计研究所摘 要:分别采用空气助燃高速热喷涂技术(HVAF)和氧气助燃高速热喷涂技术(HVOF)制备了WC-10Co4Cr涂层.通过X射线衍射仪(XRD)和扫描电子显微镜(SEM)表征和分析了不同的粉末和涂层的物相组成,微观组织结构,并对不同涂层的显微硬度,孔隙率,抗冲蚀性能进行了对比,探讨了涂层在泥沙中的冲蚀机理.结果表明:采用HVAF方法制备的涂层致密度好,其在显微硬度和抗冲蚀性能方面要优于HVOF方法制备的涂层......
HVAF喷涂WC-12Co涂层的应用研究雷国财上海宝钢工业技术服务有限公司湛江分公司摘 要:WC-12Co涂层的组织结构主要取决于喷涂工艺,采用活化燃烧一超音速火焰喷涂(HVAF)工艺喷涂WC-12Co涂层.结果表明:HVAF涂层孔隙率为0.6%,表面粗糙度为Ra1.5,HVAF过程中,粉末粒子的扁平化程度高,涂层组织结构均匀;HVAF焰流中WC基本不发生分解,涂层韧性好,HVAF涂层平均硬度达到1 400 HV0.3.关键词:HVAF;WC-12Co;粗糙度;孔隙率;硬度;韧性;......
Development of Expert Controller for Plasma Spraying Process CHEN Ke-xuan1,LI De-wu2,LI Chun-xu1,LI He-qi1 (1.Education Ministry Key Lab. of Advanced Processing Technology for Non-ferrous Materials, Lanzhou University of Science & Technology, Lanzhou, China;2.College of Materials Science and Engineering, Lanzhou Univ. of Science & Technology, Lanzhou, China) 摘要:Aiming at the plasma spraying......
plasma spray process[J]. Materials Transactions,2013, 54(2): 207-214. [17] WANG G, HUANG Z J, XIAO P, ZHU X B. Spraying of Fe-based amorphous coating with high corrosion resistance by HVAF [J..., the TiB2-SiC coating was prepared by supersonic atmospheric plasma spraying (SAPS). The effects of spraying power and spraying distance on the properties of the TiB2-SiC coating were investigated......
铜结晶器HVAF法喷涂WC-Cr3C2-Ni的试验研究朱川,吴冰阳,邹发夔,魏国东北大学冶金学院摘 要:为了提高结晶器铜板的抗磨损能力,采用空气助燃超音速火焰喷涂法(HVAF)在铜板表面喷涂WC-Cr3C2-Ni硬质合金涂层.性能测试结果表明,使用HVAF法制备的WC-Cr3C2-Ni涂层脱碳较轻,孔隙率低;具有高硬度,高耐磨性的力学性能,涂层平均显微硬度能够达到1 337HV0.3;涂层热稳定性较好,平均导热系数为292.11 W/(m·K).与目前使用的WC-17Co涂层相比,综合性能更佳.现场生产试验结果证实,WC-Cr3C2-Ni涂层的效果优于WC-17Co涂层.关键词:HVAF;WC-Cr3C2-Ni;力学性能;导热性能;......
连接层和退火对HVAF喷涂Cr3C2-NiCr涂层性能的影响陈鹏飞1,2,王学生1,2,孙华1,2,蔡飞2,张世宏21. 安徽工业大学材料科学与工程学院2. 安徽工业大学现代表界面工程研究中心摘 要:本文使用HVOF和HVAF技术在铜合金上喷涂Cr3C2-50wt%Ni Cr涂层,并就NiCr连接层和退火对HVAF喷涂层的耐磨性和耐腐蚀性进行研究.通过对涂层物相组成,显微结构,力学性能,摩擦磨损性能以及电化学动力学曲线进行测试.结果发现:HVAF喷涂层具有比HVOF更高的结合强度,且磨损体积差异较小,但致密的HVOF喷涂层其耐腐蚀性能优于HVAF喷涂层;NiCr连接层的添加提高了复合涂层的结合强度,且致密的连接层结构可阻碍腐蚀液向基体的侵蚀,使复合涂层的耐腐蚀性能提升;退火处理通过消除涂层内部缺陷提高......
......
HVAF制备WC基涂层结构与滑动摩擦磨损性能研究武笑宇,许康威,魏大岭洛阳船舶材料研究所摘 要:采用HVAF超音速火焰喷涂制备三种WC基金属陶瓷复合涂层以及金属涂层Ni60,对比分析了各涂层的微观形貌,硬度,沉积速率,滑动摩擦磨损性能.结果表明:HVAF超音速火焰喷涂制备的各涂层与基体结合良好,涂层结构致密,孔隙率<1.5%;随着复合涂层中碳化物陶瓷增强颗粒的增加,各涂层的显微硬度增大,沉积速率降低;摩擦磨损试验显示WC-10Co-4Cr,WC-12Co涂层磨损量仅为金属涂层Ni60的1/20,表现出优异的耐滑动磨损性能.关键词:HVAF;WC;摩擦磨损;......